Autor(a/res): Alex Neves Junior, Romildo Dias Toledo Filho, Jo Dweck, Eduardo de Moraes Rego Fairbairn

Resumo: After submitted to early age carbonation curing, mechanical and physical properties of high initial strength sulfate resistant Portland cement (HS SR PC) pastes were investigated, which were compared to those of non-carbonated reference pastes. Carbonation was performed for 1 and 24 hours, at the best conditions of CO2 capturing, previously determined by the authors. Despite the compressive strength and elastic modulus of the 1h carbonated pastes were slightly higher than those of the reference pastes, their absorbed water content and porosity was slightly higher than that of the reference. In the case of 24h carbonation, its compressive strength decreases significantly because of its much higher porosity, although the new solid carbonated calcium silicate phase presents a much higher specific mass than those of the solid phases of the 1 hour and non-carbonated pastes.