Autor(a/res): Fabrício de C. Vitorino, Romildo D. Toledo Filho & Jo Dweck

Resumo: Oil well cementing is a vital operation to assure casing stability and zonal isolation for oil and gas exploration. However, some scenarios demand the cemented region to withstand high thermal gradients and imposed deformations, as occurs in the case of oil wells subjected to cyclic steam injection at temperatures up to 250 °C, to reduce oil viscosity and to increase well pressure to facilitate heavy oil recovery. In this paper, the hydration of ductile special cement systems using styrene-butadiene latex (SBR) and carboxylated styrene-butadiene latex (XSBR) addition was studied by conduction calorimetry. The resulting heat flow curves, presented in log–log plots, were used to analyze the influence of those copolymers on the hydration stages of three families of cement pastes of different complexity. The simpler cement systems (SCCS) contained water, oil well Portland cement class G and SBR or XSBR in its composition. In medium complexity systems silica fume was added and in the higher complexity ones (HCCS), superplasticizer as well. The primary objective of adding those copolymers into the Portland cement paste is to obtain higher ductility properties after setting, silica fume to have good thermal stability up to 300 °C, while superplasticizer was added to guarantee good workability. Rheological tests were carried out to evaluate the effect of the copolymers on the composite viscosity. Thermogravimetric analysis of selected SCCS and HCCS samples was performed to quantify the main formed phases up to 24 h of cement hydration. From the obtained results, it was noticed that SBR and XSBR addition substantially affects hydration kinetics at all early age stages. Starting from pre-induction and induction periods, the main observed effect during these stages, was related to the increased viscosity of the pastes, which was higher in XSBR containing pastes, retarding the hydration reactions of respective following stages, when compared to pastes with the same cementitious matrix without copolymer addition.

Acesse AQUI e confira o artigo.